W1.2311 – Steels For Molds Tools And Die

Short Description:

A HRC 40 prehardened mould steel (300 HB/32 HRC) W1.2311 is a 300 HB (32 HRC) prehardened grade specially designed for plastic mold industry. Chromium, Molybdenum and Manganese additions are optimized to have a fully martensite – bainite microstructure after quenching. The steel is melted in an electrical furnace and refined with VOD or DH device. The cleanliness of the steel is guaranteed as well as the soundness. This makes the steel particularly well adapted for mold steel even when polish...


Product Detail

Product Tags

A HRC 40 prehardened mould steel (300 HB/32 HRC)

W1.2311 is a 300 HB (32 HRC) prehardened grade specially designed for plastic mold industry. Chromium, Molybdenum and Manganese additions are optimized to have a fully martensite – bainite microstructure after quenching.

The steel is melted in an electrical furnace and refined with VOD or DH device. The cleanliness of the steel is guaranteed as well as the soundness. This makes the steel particularly well adapted for mold steel even when polishing or chemical etching are required for surface finish quality.

Standard
? EN: 40 CrMnMo7
? WERKSTOFF Number: 1.2311
? AISI: ≈ P20

Chemical Analysis
Typical values (weight%)

C S max P max Si Mn Cr Mo
.4 .005 .012 3 1.5 1.9 2

Mechanical Properties

Hardness YS 0.2 UTS Elongation Reduction
of area
Elastic modulus
HB MPa ksi MPa ksi % Z% GPa ksi
Longitudinal
direction
300 854 124 1014 147 10.8 50 205 29745
Longitudinal
direction
300 821 119 992 144 9.6 48 205 29745

Delivery Conditions
Dimensional program

Thickness Width
20 – 120 mm
(.79″ – 4.7″)
1500 – 2500 mm
(59″ – 98.4″)
120 – 350 mm
(4.7″ – 14″)
1500 – 2100 mm
(49″ – 82.7″)

PDF: http://www.industeel.info/wp-content/http://www.bz-aluminium-steels.com/uploads/uploads/2016/01/DS-MOLD-W12311.pdf


  • Previous:
  • Next:

  • Send your message to us:

    INQUIRY NOW
    • * CAPTCHA: Please select the House

    Related Products

    INQUIRY NOW
    • * CAPTCHA: Please select the Cup